Aramid fabric ballistic 200 g/m² (plain weave) 130 cm

USA: width 51.18", weight 5.9 oz/yd²

Low-modulus Aramid fibers such as those used in ballistic aramid fabric have a high work absorption capacity and are used for protective clothing and ballistic hard laminates as well as splinter and bullet protection vests.

Fibre: Low-modulus Aramid 840 den, 93 tex
Weave type: Plain
Warp: Aramid 840 den 93 tex, 10.5 ends/cm
Weft: Aramid 840 den 93 tex, 10.5 ends/cm
Width: 130 cm

Technical data:
Elongation at Break: 3,5 % ± 0.5
Tensile strenght: 3423 MPa ± 254
E-Modulus: 89 GPa ±9
Maximum Force Warp: > 8000 N/5 cm
Maximum Force Weft: > 8500 N/5 cm
Heat resistance (residual strength after 48 h at 200 °C): 90 %
Decomposition temperature: > 450 °C
Coeffizient of thermal expansion linear: -3,5 % 10^-6/K

Application:
For the production of a wide range of cut-resistant safety clothing, accessories and equipment. In the automotive industry e.g. splinter protection, ballistics for protective waistcoats or armour plates or generally in laminates as tear-out protection for drill holes or inserts.

Calculated data for hand laminates with 35 volume percent fibres:
Resin consumption: 294 g/m², laminate thickness: 0.39 mm, laminate weight: 494 g/m²